It is produced according to the requirements of GB/T75 9 4.7-8 7 and meets the requirements of the coal industry standard MT8 18-2009.
It is used for heavy-duty cable jackets with long-term allowable operating temperature of 65 °C. It has high strength. It is oil-resistant, heat-resistant, ozone-resistant and flame-retardant. The cable is especially suitable for long-term use in harsh working environments, and can completely replace the neoprene (C R) compound. The performance of the red and yellow cable sheathing materials produced by the company meets the requirements of GB 1 29 7 2-9 1 standard.
| Before aging | Tensile strength ≥ | Mpa | 11.0 | 12.5 | |
| Elongation at break ≥ | ％ | 250 | 480 | ||
| Air box aging test | Aging condition | temperature | ℃ | 75±2 | 75±2 |
| time | 10×24 | 10×24 | |||
| Tensile strength after aging | ≥ | Mpa | ／ | 13.6 | |
| Rate of change ≤ | ％ | -15 | 8.8 | ||
| Elongation at break after aging | ≥ | ％ | 200 | 470 | |
| Rate of change ≤ | ％ | -25 | -6.1 | ||
| Thermal extension test | Test conditions | Air temperature | ℃ | 200±3 | 200±3 |
| Load time | min | 15 | 15 | ||
| Mechanical stress | N／cm2 | 20 | 20 | ||
| Elongation under load ≤ | ％ | 175 | 15 | ||
| Permanent deformation after cooling ≤ | ％ | 25 | 0 | ||
| Oil immersion test | Test conditions | Oil temperature | ℃ | 100±2 | 100±2 |
| Oil immersion test | H | 24 | 24 | ||
| Tensile strength change rate ≤ | ％ | -40 | 3.9 | ||
| Elongation at break elongation rate ≤ | ％ | -40 | -10 | ||
| Tear test | Tear strength ≥ | N/mm | 7.0 | 8.5 | |
| Oxygen Index | 38 | ||||
| proportion | Maximum | g/cm3 | 1.545 | ||
Mining cable sheathing compound 2019-8-30 本文被閱讀 2816 次
| PREV:Wire and cable model name | NEXT:Marine cable sheathing compound (XH-21A) |
Contact: Manager Zhang
Mobile: 18660668323
Landline: 0536-7371003
Company Address: Hanting District, Weifang City, Shandong ProvinceLingang Logistics Industrial Park South Road